Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL GTX™ Resin NX0031 - Americas - (PPE+PA*) - Saudi Basic Industries Corporation (SABIC)

Check here, which other Noryl GTX datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding - 機能

Any use of this information falls under the rules of our disclaimer.

商品の説明文

NORYL GTX™ NX0031 resin is a non-reinforced alloy of PPE/PA. This conductive, injection moldable grade exhibits high heat resistance, excellent chemical resistance, and high impact resistance. NORYL NX0031 resin was designed for electrostatic painting and powder coating without the need for a conductive primer. This material can also be solvent painted and is an excellent for candidate for exterior, painted applications such as trim and fairings for outdoor vehicles, motorcycle, heavy truck, bus, personal watercraft, and marine. It is available only in black.

UL Yellow Card Link E121562-533883

Processing/Physical Characteristics	値	単位	テスト基準
ISO データ
メルトボリュームレイト, MVR	8	cm³/10min	ISO 1133
温度	280	°C	-
荷重	5	kg	-
溶融時の熱伝導率	0.22	W/(m K)	-
溶融時の比熱	2200	J/(kg K)	-
突き出し時の時の温度	130	°C	-
ASTM数据
メルトフローレイト, MFI	8	g/10min	ASTM D 1238
温度	280	°C	-
荷重	5	kg	-

機械的特性	値	単位	テスト基準
ISO データ
引張弾性率	2000	MPa	ISO 527
降伏応力	50	MPa	ISO 527
降伏ひずみ	4	%	ISO 527
破壊応力	48	MPa	ISO 527
破壊ひずみ	30	%	ISO 527
曲げ弾性率	1900	MPa	ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C	18	kJ/m²	ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30ﾟC	10	kJ/m²	ISO 179/1eA
ノッチ付きアイゾット衝撃強さ, +23°C, 4mm	20	kJ/m²	ISO 180/1A
ノッチ付きアイゾット衝撃強さ, -30°C, 4mm	10	kJ/m²	ISO 180/1A
ASTM数据
引張弾性率	2250	MPa	ASTM D 638
降伏応力	52	MPa	ASTM D 638
破壊応力	48	MPa	ASTM D 638
降伏点伸び	5	%	ASTM D 638
破断伸び	34	%	ASTM D 638
曲げ弾性率	2100	MPa	ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in	224	J/m	ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature	117	J/m	ASTM D 256
温度	-30	°C	-

熱的特性	値	単位	テスト基準
ISO データ
ビカット軟化温度, B	175	°C	ISO 306
ビカット軟化温度, 120°C/h 50N	180	°C	ISO 306
線膨張係数, 平行	100	E-6/K	ISO 11359-1/-2
線膨張係数, 直角	90	E-6/K	ISO 11359-1/-2
1.5mm厚さでの燃焼性	HB	class	IEC 60695-11-10
試験片の厚さ	1.5	mm	-
ASTM数据
DTUL @ 66 psi	176	°C	ASTM D 648
DTUL @ 264 psi	136	°C	ASTM D 648
ビカット軟化温度	175	°C	ASTM D 1525

その他の特性.	値	単位	テスト基準
吸水率.	4.2	%	Sim. to ISO 62
吸湿率	1.2	%	Sim. to ISO 62
密度.	1090	kg/m³	ISO 1183
密度	1090	kg/m³	ASTM D 792

Processing Recommendation Injection Molding	値	単位	テスト基準
Pre-drying - Temperature	95 - 105	°C	-
Pre-drying - Time	3 - 4	h	-
Processing humidity	≤0.07	%	-
樹脂温度	270 - 295	°C	-
金型温度	65 - 95	°C	-
Zone 1	255 - 295	°C	-
Zone 2	260 - 295	°C	-
Zone 3	265 - 295	°C	-
Screw speed	20 - 100	rpm	-
Back pressure	0.3 - 1.4	MPa	-

機能

特殊な特性

成形加工法.

射出成形.

領域別の利用可能性

北アメリカ.

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.